Poled polyureasulfone thin films having excellent transparency from near UV to visible region have been prepared by carrying out additional polymerization of 1,4- phenylene diisocyanate and 4,4'-diaminodiphenyl sulfone simultaneously with poling. The polymerization process is monitored by in-situ second harmonic generation. Under optimal conditions, d33 as large as 8.5 pm/V at a second harmonic wavelength of 532 nm has been obtained. SHG intensity decreased to about 84% of its initial value after having been kept at 100 degrees Celsius for over 1000 hours. Wavelength dispersion measurement of SHG coefficients indicates that d33 of prepared poled films increases by about a factor of three at a second harmonic wavelength of 400 nm.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.