In-situ atomic-force microscopy of laser-conditioned and laser-damaged HfO2/SiO2 dielectric mirror coatings

Michael C. Staggs; Mehdi Balooch; Mark R. Kozlowski; Wigbert J. Siekhaus

doi:10.1117/12.60129

29 July 1992 In-situ atomic-force microscopy of laser-conditioned and laser-damaged HfO2/SiO2 dielectric mirror coatings

Michael C. Staggs, Mehdi Balooch, Mark R. Kozlowski, Wigbert J. Siekhaus

Author Affiliations +

Proceedings Volume 1624, Laser-Induced Damage in Optical Materials: 1991; (1992) https://doi.org/10.1117/12.60129
Event: Laser-Induced Damage in Optical Materials: 1991, 1991, Boulder, CO, United States

Abstract

Atomic force microscopy was used to determine in-situ the nm-scale morphological changes that occur on dielectric optical coatings as a result of laser illumination. Of particular interest is a process called laser conditioning in which the damage threshold of the films is increased by a factor of 2 to 3 when the film is first illuminated at fluences below the damage threshold. The optical coating studied was a highly refractive dielectrical multilayer mirror (HR) consisting of many alternating quarter-wave layers of HfO₂ and SiO₂ at 1.06 micrometers . The top layer was a (lambda) /2 SiO₂ overcoat. Laser beam specifications were: 1.06-micrometers wavelength, 8- to 10-ns pulsewidth. Laser beam spot sizes ranging from 85 micrometers to 1.4 mm in diameter. The maximum scan range of the AFM was 80 micrometers . A survey of the as-deposited surface shows mostly hillocks approximately 200 nm in diameter and 10 nm in height. The predominant surface irregularity is micrometers -scale domes associated with the well known nodule defects. Laser illumination causes nodule defects to be easily ejected from the coating surface. Further damage may propagate from the resulting craters. These nodule defects therefore determine the damage threshold of the film. Using the AFM we have shown that for illumination at fluences below the nodule ejection threshold we observe a decrease in the surface roughness of the nodule defects and hillock structure of the as-deposited film. The subtle changes in these surface features may be an indication that the film is being mechanically stabilized, thus providing the observed conditioning effect.

Citation Download Citation

Michael C. Staggs, Mehdi Balooch, Mark R. Kozlowski, and Wigbert J. Siekhaus "In-situ atomic-force microscopy of laser-conditioned and laser-damaged HfO2/SiO2 dielectric mirror coatings", Proc. SPIE 1624, Laser-Induced Damage in Optical Materials: 1991, (29 July 1992); https://doi.org/10.1117/12.60129

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available