Cure rate and dry etch patterning of thermoset polymers

Maria-Jose Montoya; Darren Simon; Anthony Stephen Holland; Robert Shanks

doi:10.1117/12.582302

23 February 2005 Cure rate and dry etch patterning of thermoset polymers

Maria-Jose Montoya, Darren Simon, Anthony Stephen Holland, Robert Shanks

Proceedings Volume 5650, Micro- and Nanotechnology: Materials, Processes, Packaging, and Systems II; (2005) https://doi.org/10.1117/12.582302
Event: Smart Materials, Nano-, and Micro-Smart Systems, 2004, Sydney, Australia

Abstract

High quality thermoset polymer solutions are available from several commercial suppliers. These are suitable for forming thin films for optical waveguides because of their high transmission, suitable refractive indices and thickness uniformity of films obtained by spinning solutions on a substrate such as silicon. The solution's viscosity and the spinning speed determine the thickness of resulting films. The plasma etch rate was examined for trenches (of the order of 1 μm depth, suitable for photonic waveguide fabrication) formed in such films from a relatively high viscose polymer solution (UV15 from Master Bond). The cross-link density of the polymer is dependent on its curing process, that is, the exposure to ultra-violet light radiation and heat. The curing process can have a profound affect on the etch rate. Different paths were taken in the curing and etching process of the spun polymer film in order to examine the relation between the cross-link density and the polymer etching process. We examine the polymer films using FTIR to qualitatively measure the cross-link density and DSC for changes in the glass transition temperature (Tg). FTIR is used to show if chemical changes occur for different levels of curing. Determining Tg is important because this will show how it changes with the baking step. We have observed that for films with low Tg, the plasma etch process can cause the polymer surface to flow and hence wrinkle. Post-curing at higher temperatures increases Tg. By choosing appropriate curing steps, Tg and the etch rate can be optimized to obtain an optimum etch rate and preserve the smooth polymer surface during etching.

Citation Download Citation

Maria-Jose Montoya, Darren Simon, Anthony Stephen Holland, and Robert Shanks "Cure rate and dry etch patterning of thermoset polymers", Proc. SPIE 5650, Micro- and Nanotechnology: Materials, Processes, Packaging, and Systems II, (23 February 2005); https://doi.org/10.1117/12.582302

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available